S-Plastic Thermocomp MF006S LNP* Thermocomp* MF006S is a compound based on Polypropylene resin containing Glass Fiber. Adde

Product Categories

Ultem PEI Resin [197]
Cycoloy PC ABS [9]
Xenoy Resin [2]
Cycolac ABS [173]
Geloy Resin [110]
Colorcomp [20]
LNP Faradex [37]
S-Plastic Lubricomp [506]
LNP Stat Kon [308]
S-Plastic Thermocomp [705]
Plastic Resin Pellets Bulk [113]
Verton Plastic [106]

Shenzhen Samtion Chemical Co., Ltd

Contact Now

S-Plastic Thermocomp MF006S LNP* Thermocomp* MF006S is a compound based on Polypropylene resin containing Glass Fiber. Adde

Name: SPlastic Thermocomp MF006S LNP Thermocomp MF006S is a compound based on Polypropylene resin containing Glass Fiber Adde
Brand: S-Plastic Thermocomp
Price: 1 USD

Quality S-Plastic Thermocomp MF006S LNP* Thermocomp* MF006S is a compound based on Polypropylene resin containing Glass Fiber. Adde for sale

Brand Name : S-Plastic Thermocomp

Model Number : MF006S

Certification : COA/ICP Test/Rohs/MSDS

Place of Origin : ——

MOQ : 100KG

Price : *USD

Payment Terms : L/C, T/T, Western Union, MoneyGram

Supply Ability : To be negotiated

Delivery Time : To be negotiated

Packaging Details : 25KG/bag

Melt Volume Rate, MVR at 260°C/2.16 kg : ？？？

UL Recognized, 94HB Flame Class Rating (3) : ？？？

Contact Now

S-Plastics Thermocomp MF006S resin is LNP* Thermocomp* MF006S is a compound based on Polypropylene resin containing Glass Fiber. Added features of this material
include: Heat Stabilized

Property

TYPICAL PROPERTIES (1)
MECHANICAL	Value	Unit	Standard
Tensile Stress, break	81	MPa	ASTM D 638
Tensile Strain, break	1.8	%	ASTM D 638
Tensile Modulus, 50 mm/min	14470	MPa	ASTM D 638
Flexural Stress	131	MPa	ASTM D 790
Flexural Modulus	6200	MPa	ASTM D 790
Tensile Stress, break	80	MPa	ISO 527
Tensile Strain, break	3	%	ISO 527
Tensile Modulus, 1 mm/min	9120	MPa	ISO 527
Flexural Stress	135	MPa	ISO 178
Flexural Modulus	6800	MPa	ISO 178
IMPACT	Value	Unit	Standard
Izod Impact, unnotched, 23°C	603	J/m	ASTM D 4812
Izod Impact, notched, 23°C	53	J/m	ASTM D 256
Izod Impact, unnotched 80104 +23°C	37	kJ/m²	ISO 180/1U
Izod Impact, notched 80104 +23°C	5	kJ/m²	ISO 180/1A
THERMAL	Value	Unit	Standard
HDT, 0.45 MPa, 3.2 mm, unannealed	157	°C	ASTM D 648
HDT, 1.82 MPa, 3.2mm, unannealed	133	°C	ASTM D 648
CTE, -40°C to 40°C, flow	6.84E-05	1/°C	ASTM E 831
CTE, -40°C to 40°C, xflow	4.5E-05	1/°C	ASTM E 831
CTE, -40°C to 40°C, flow	6.9E-05	1/°C	ISO 11359-2
CTE, -40°C to 40°C, xflow	4.4E-05	1/°C	ISO 11359-2
HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm	161	°C	ISO 75/Bf
HDT/Af, 1.8 MPa Flatw 80104 sp=64mm	141	°C	ISO 75/Af
PHYSICAL	Value	Unit	Standard
Density	1.12	g/cm³	ASTM D 792
Mold Shrinkage, flow, 24 hrs	0.6 - 0.8	%	ASTM D 955
Mold Shrinkage, xflow, 24 hrs	0.9 - 1.1	%	ASTM D 955
Mold Shrinkage, flow, 24 hrs	0.65	%	ISO 294
Mold Shrinkage, xflow, 24 hrs	0.98	%	ISO 294
Density	1.12	g/cm³	ISO 1183
Source GMD, last updated:09/24/2008

Processing

Parameter
Injection Molding	Value	Unit
Drying Temperature	80	°C
Drying Time	4	hrs
Melt Temperature	225 - 250	°C
Front - Zone 3 Temperature	240 - 250	°C
Middle - Zone 2 Temperature	215 - 225	°C
Rear - Zone 1 Temperature	195 - 205	°C
Mold Temperature	30 - 50	°C
Back Pressure	0.2 - 0.3	MPa
Screw Speed	30 - 60	rpm
Source GMD, last updated:09/24/2008

Other related products we recommend:

For more information please download the datesheet
	S-Plastics Thermocomp MF006S.pdf

Get The Latest Quotation

First-level distribution source in South China

Reduce procurement costs, improve supply stability,

Help you find the most suitable engineering plastic materials

Click to consult and get the latest quotation within 24 hours!

Product Tags:

Thermocomp S-Plastic Thermocomp

S-Plastic S-Plastic Thermocomp