S-Plastic Stat-kon AD000 ABS, Carbon, Property

Name: SPlastic Statkon AD000 ABS Carbon Property
Brand: S-Plastic Stat-kon
Price: 1 USD

Quality S-Plastic Stat-kon AD000 ABS, Carbon, Property for sale

Brand Name : S-Plastic Stat-kon

Model Number : AD000

Certification : COA/ICP Test/Rohs/MSDS

Place of Origin : ——

MOQ : 100KG

Price : *USD

Payment Terms : L/C, T/T, Western Union, MoneyGram

Supply Ability : To be negotiated

Delivery Time : To be negotiated

Packaging Details : 25KG/bag

Melt Volume Rate, MVR at 260°C/2.16 kg : ？？？

UL Recognized, 94HB Flame Class Rating (3) : ？？？

Contact Now

S-Plastics Stat-kon AD000 resin is ABS, Carbon,Property

Property

TYPICAL PROPERTIES (1)
MECHANICAL	Value	Unit	Standard
Tensile Stress, yld, Type I, 5 mm/min	31	MPa	ASTM D 638
Tensile Stress, brk, Type I, 5 mm/min	29	MPa	ASTM D 638
Tensile Strain, yld, Type I, 5 mm/min	2	%	ASTM D 638
Tensile Strain, brk, Type I, 5 mm/min	6.4	%	ASTM D 638
Tensile Modulus, 50 mm/min	2380	MPa	ASTM D 638
Flexural Stress, brk, 1.3 mm/min, 50 mm span	59	MPa	ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span	2480	MPa	ASTM D 790
Tensile Stress, yield, 5 mm/min	30	MPa	ISO 527
Tensile Stress, break, 5 mm/min	28	MPa	ISO 527
Tensile Strain, yield, 5 mm/min	1.5	%	ISO 527
Tensile Strain, break, 5 mm/min	3.9	%	ISO 527
Tensile Modulus, 1 mm/min	2310	MPa	ISO 527
Flexural Modulus, 2 mm/min	2510	MPa	ISO 178
IMPACT	Value	Unit	Standard
Izod Impact, unnotched, 23°C	369	J/m	ASTM D 4812
Izod Impact, notched, 23°C	25	J/m	ASTM D 256
Izod Impact, unnotched 80104 +23°C	22	kJ/m²	ISO 180/1U
Izod Impact, notched 80104 +23°C	2	kJ/m²	ISO 180/1A
THERMAL	Value	Unit	Standard
HDT, 0.45 MPa, 3.2 mm, unannealed	94	°C	ASTM D 648
HDT, 1.82 MPa, 3.2mm, unannealed	80	°C	ASTM D 648
CTE, -40°C to 40°C, flow	8.01E+00	1/°C	ASTM E 831
CTE, -40°C to 40°C, xflow	8.81E+00	1/°C	ASTM E 831
HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm	94	°C	ISO 75/Bf
HDT/Af, 1.8 MPa Flatw 80104 sp=64mm	80	°C	ISO 75/Af
PHYSICAL	Value	Unit	Standard
Density	1.119	g/cm³	ASTM D 792
Moisture Absorption, 50% RH, 24 hrs	0.22	%	ASTM D 570
Mold Shrinkage, flow, 24 hrs	0.3 - 0.5	%	ASTM D 955
Mold Shrinkage, xflow, 24 hrs	0.3 - 0.5	%	ASTM D 955
Density	1.11	g/cm³	ISO 1183
Moisture Absorption (23°C / 50% RH)	0.33	%	ISO 62
Source GMD, last updated:02/04/2008

Processing

Parameter
Injection Molding	Value	Unit
Drying Temperature	70 - 80	°C
Drying Time	4	hrs
Maximum Moisture Content	0.05 - 0.1	%
Melt Temperature	200 - 210	°C
Front - Zone 3 Temperature	205 - 215	°C
Middle - Zone 2 Temperature	195 - 205	°C
Rear - Zone 1 Temperature	180 - 195	°C
Mold Temperature	10 - 50	°C
Back Pressure	0.2 - 0.3	MPa
Screw Speed	30 - 60	rpm
Source GMD, last updated:02/04/2008

Other related products we recommend:

For more information please download the datesheet
	S-Plastics Stat-kon AD000.pdf

Get The Latest Quotation

First-level distribution source in South China

Reduce procurement costs, improve supply stability,

Help you find the most suitable engineering plastic materials

Click to consult and get the latest quotation within 24 hours!